White Granule Polymer Paper Sizing Chemicals Polyvinyl Alcohol PVA 1799 is a few kind of synthetic with water soluble high-molecular polymer. The main specification includes degree of polymerization & alcoholysis and other special performance. Polyvinyl Alcohol is manufactured by polymerization of vinyl acetate in methanol solvent, then undergoing alcoholysis via advanced belt-process of low-alkali. After grinning, drying and packing, the end PVA products are achieved.
Ürün Parametresi (Spesifikasyon)
| Öğe | PVA 1799 |
| Hidroliz (mol %) | 98.0 ~ 99.9 |
| Viskozite (mPa.s) | 22.0 ~ 30.0 |
| Uçucu (wt%) | ≤ 5.0 |
| Kül (wt%) | ≤ 0.5 |
| pH Değeri | 5 ~ 7 |
| Saflık (%) | ≥ 91.5 |
| Parçacık Boyutu | Pul, 10 ~ 80mesh |
Eşdeğer Notlar:
100-27
Kuraray PVA-105
Kuraray Mowiol 30-98
CCP PF-05
Sekisui Selvol 325 - Celanese
JVP JF-17L
Nichigo NL-18
Main Apprication:
1. Tekstil Endüstrisinde pamuk veya suni ipek ipliği için Çözgü Haşıllama Maddesi.
2. Paper surface sizing, Paper adhesive, Pigment binding, Resin Finishing Agent.
3. Modifier for Thermosetting Resins, Protective colloid for PVAc emulsion.
5. Cold Water Insoluble PVA film, Butyralized PVA , Adhesive for Ceramic Resister and Plug.
4. Adhesive for Forming Board in Architecture, PVA Sponge, EmeryWheel and Grinding Material.
6. Temporary Protective coating for PVC sheet, Plywood, Acrylate Sheet.
7. PVA Sheet, Hose, Roller, Tube, Belt,
Paketleme: İçinde plastik film bulunan kraft kağıt ambalaj, torba başına 20kg/25kg veya torba başına 500KG dokuma torba.
Depolama: Ürünler, oda sıcaklığının 5-30 ℃ olduğu, kuru ve iyi havalandırılan bir yerde, partiler halinde depolanmalıdır. Güçten uzak tutun, nemi önleyin ve güneşe maruz kalmaktan kaçının. Adsorpsiyonun bozulmasını önlemek için uçucu kimyasallarla birlikte depolanması kesinlikle yasaktır.